Crystallographic Structural and Magnetic Propertiesof FePt Nanoparticles

Fe 60Pt 40nanoparticles have been successfully prepared by sonochemistry method from the solution of Fe(C2H3O2)2and H 2PtCl 6. The as-prepared sample then has been annealed at temperatures from 450 o C to 650 o C. Annealed samples have ordered L1ophase with face-centered tetragonal (fct) structure and show hard magnetic properties. The nanoparticles annealed at 550 o C show highest coervicity of 4.36 kOe measured at room temperature. The annealed-temperature dependence of the coercivity is consistent with theappearance of the order phase L1 oin the samples.